可降解皮肤缝合器
taple Diameter
Breakdown strength* (in vitro) 1.7 kg at the first day
Maintain more than 80% of the its original strength in 2 weeks
Degradation rate (in vitro)
(Following ISO 10993-15) 0.18 mm/y
Degradation rate (in vivo) N.D. (Remove while healing)
*Tested with artificial models
可降解止血夹
Cross section
Tolerable fluid
pressure* >32 KPa
Peel force* > 0.15 kg
Degradation rate (in vitro)
(Following ISO 10993-15) 0.18 mm/y
Degradation rate (in vivo) 0.47~0.71 mm/y
About 10~15 weeks
*Test on Ø3 mm silica tube
可降解镁合金原材料
Materials Magnesium alloy
Type1 Circular Wire
(Ø0.05 mm~Ø1.5 mm)
Type2 Square Wire
(0.5 mm (Min.) ~1.5 mm (Max.))
Corrosion rate 0.15~0.5 mm/y (Adjustable)
小批量客制件服务
小样品打样